Hot Forged Carbon Steel Ring , AISI 1035 / S35C Steel Grade Forged Rings 

Professional AISI 1035/S35C Carbon Steel forged steel rings

Applications

The following are the major applications of AISI 1035 carbon steel:

• Levers
• Bolts
• Nuts
• Studs

Introduction

Carbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% silicon and 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium and nickel are present in these steels.

AISI 1035 is a water resisting carbon steel whose wear resistance and hardenability are increased by the addition of small quantity of chromium.

The following sections will discuss in detail about AISI 1035 carbon steel.

Category Steel Class Carbon steel Type Standard Designations France: AFNOR CC 35 Germany: DIN 1.0501 Italy: UNI C 35 Sweden: SS 1550 United Kingdom: B.S. 060 A 35 , B.S. 080 A 32 , B.S. 080 A 35 , B.S. 080 A 37 , B.S. 080 M 36 United States: AMS 5080 , AMS 5080D , AMS 5082 , AMS 5082A , ASTM A108 , ASTM A29 , ASTM A510 , ASTM A519 , ASTM A544 , ASTM A545 , ASTM A546 , ASTM A576 , ASTM A682 , FED QQ-S-635 (C1035) , FED QQ-S-700 (1035) , SAE J403 , SAE J412 , SAE J414 , UNS G10350 Composition Element Weight % C 0.32-0.38 Mn 0.60-0.90 P 0.04 (max) S 0.05 (max) Mechanical Properties Properties Conditions T (°C) Treatment Density (×1000 kg/m3) 7.7-8.03 25 Poisson's Ratio 0.27-0.30 25 Elastic Modulus (GPa) 190-210 25 Tensile Strength (Mpa) 485 25 cold drawn (round bar (50-75 mm)) more Yield Strength (Mpa) 415 Elongation (%) 10 Reduction in Area (%) 30 Hardness (HB) 143 25 cold drawn (round bar (50-75 mm)) more

HEAT TREATMENT

Heat treatment is carried out on this grade to render it suitable for machining and to impart to it specified mechanical properties.

ANNEALING

Full annealing of small C1035 forgings is carried out between 1550 and 1625 º F (840 – 890 º C) followed by furnace cooling at 50 º F (10 º C) per hour, to 1200 º F (650 º C) and air cooling.

NORMALIZING

The normalizing temperature range for this grade is typically 1600 – 1650 º F (870 – 900 º C,) Normalizing is followed by cooling in still air. When forgings are normalized before hardening and tempering or other heat treatment, the upper range of the normalizing temperature is used. When normalizing is the final treatment, the lower temperature range is used.

HARDENING

Hardening of this grade is carried out from an austenitizing temperature of 1525 – 1575 º F (830 – 860 º C) and oil or water quenching.

Flame and induction hardening may be carried out by heating quickly to the desired case depth and quenching in water or oil. This should be followed by a tempering treatment at 300 – 400 º F (150 – 200 º C) to reduce stresses in the case without affecting its hardness. A surface hardness of Rc 50 may be obtained by this treatment.

TEMPERING

Tempering after normal hardening and oil or water quenching is carried out at 750 – 1260 º F (400 – 680 º C) to give the required mechanical properties as determined by practical experience.

MACHINABILITY

Machinability of C1035 is good providing the full annealing cycle described above is used, ensuring a coarse lamellar pearlite to coarse spheroidite microstructure.

WELDABILITY

This grade is readily welded with the correct procedure. Welding in the through-hardened or flame or induction-hardened conditions is not recommended.

Low-hydrogen electrodes are recommended together with preheat at 300 – 500 º F (150 – 260 º C.) to be maintained during welding, Cool slowly and stress relieve where possible.

 We, Shanghai Unite Steel are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national famous steel enterprise.

In the aspect of resources and information, we have established cooperative and stronger relationship with nearly hundred enterprises, either state-owned or private owned in china, such as: DAYE Special Steel-a famous steel enterprise with the longest steelmaking history; BAO Steel, and Dongbei Special Steel Group-the biggest special steel manufacturer; TPCO, VALIN-largest seamless steel tube production enterprise; What's more, we have built long, deep and close business relationship with dozens of steel companies, Sharing and holding equities with several steel enterprises. Because of the close cooperation with steel companies and our pioneering spirit, which can ensure us stay at the top competition, and ensure our customers get what they really want!