EN36A Heavy - Duty Gears Forged Steel Rings Black / Bright / Polished Surface

EN36A/15NiCr13/X3312H high-quality hot forged steel rings

Description:
EN36 is an alloy case hardening steel. Characteristics of the steel are toughness arising from the use of nickel and a more uniform hardness produced by the use of chromium. It is specifically designed for carburising to give a very hard case with a strong core.

APPLICATIONS:

Heavy Duty Bushings, Collets, Conveyor Pins, Heavy Duty Gears, King Pins, Ring Gears, Sprockets, Shafts, heavy-duty gears, collets etc. Or can be used for high tensile applications uncarburised but through hardened and tempered.

Related Specifications:

Australia AS 1444-1996-X3312/X3312H

Germany W.Nr 1.5752 DIN 14NiCr14

Great Britain BS970: PART 3: 1991 655 M13

BS970: 1955 - EN36A

EN10084-1998 1.5752 15NiCr13 or

1.5752H 15NiCr13H

Japan JISG 4052 SNC815H

JISG 4102 SNC815

U.S.A. SAE 3310 9310

AISI E3310 E9310

UNS G33106/G93106

Chemical Composition(%):

Carbon 0.10-0.16

Silicon 0.10-0.40

Manganese 0.35-0.60

Nickel 3.00-3.75

Chromium 0.70-1.00

Phosphorous 0.04 max

Sulphur 0.04 max

Process: EAF+LF+VD+Forged+Heat Treatment(optional)

SIZE RANGE:

OD up to 8,000mm; ID up to 7,800mm; Thickness up to 500mm

SURFACE FINISHES:

Black, Peeled (K12), Turned & Polished (H10, H11)

Ultrasonic test :ASTM A 388 or according to customers' requirement

Heat Treatment:

Carburising Temperature
Heat to 890°C/920°C and soak for the necessary time to obtain the desired carburised depth.
Single Quench Treatment:
Heat the carburised parts to 800/820°C and quench in oil.
Double Quench Treatment:
Heat the carburised parts to 850/880°C, cool in oil or air then re heat to 760/780C and quench in oil.
Tempering:
After hardening temper at 150°C for 2 hours minimum, and allow to cool in air to give a final surface hardness in the region of Rockwell C60/62.

Certificate of Quality: issued in English, in addition the normal terms, production process, the mechanical property (yield strength, tensile strength, elongation and hardness), forged ratio, UT test result, Grain size, heat treatment methods and the sample of is shown on the Certificate of Quality.

Marking: Heat No. will be cold stamped and Steel grade, diameter (mm), length (mm), and the manufacturer LOGO and weight (kg) is painted

 We, Shanghai Unite Steel are committed to integrate engineering steel resources in china and serve the global engineering steel market. Our company has more than 15 years of experience in steel researching, production, managing and sales. And our team mostly are based on and worked in national famous steel enterprise.

In the aspect of resources and information, we have established cooperative and stronger relationship with nearly hundred enterprises, either state-owned or private owned in china, such as: DAYE Special Steel-a famous steel enterprise with the longest steelmaking history; BAO Steel, and Dongbei Special Steel Group-the biggest special steel manufacturer; TPCO, VALIN-largest seamless steel tube production enterprise; What's more, we have built long, deep and close business relationship with dozens of steel companies, Sharing and holding equities with several steel enterprises. Because of the close cooperation with steel companies and our pioneering spirit, which can ensure us stay at the top competition, and ensure our customers get what they really want!